 Nitrile
Rubber
Due to the consistent high quality of products and commitment to
the U. S. Market, our Russian suppliers have been particularly effective
in creating value for our North American customers.
| |
Grade
15M |
Grade
18 |
Grade
18M |
Grade
25 |
Grade
25M |
Mooney
viscosity
ML 1+4 @ 100°C |
|
80-120 |
43-45 |
80-120 |
|
| ·
group 1 |
43-55 |
|
43-55 |
|
43-55 |
| ·
group 2 |
58-68 |
|
58-68 |
|
58-68 |
Tensile
strength,
MPa, min |
17.6 |
18.6 |
17.6 |
24 |
23.5 |
Elongation
at break,
%, min |
450 |
450 |
450 |
425 |
450 |
| Toluene
%, max |
70 |
65 |
65 |
40 |
40 |
| ash
content, %, max |
0.6 |
0.6 |
0.6 |
0.6 |
0.6 |
| Mass
loss on drying, % |
0.8 |
0.8 |
0.8 |
0.8 |
0.8 |
Antioxadant
total
mass, %: |
0.2-0.3 |
0.2-0.3 |
0.2-0.3 |
0.2-0.3 |
0.2-0.3 |
| Organic
acid, % max |
4 |
4 |
4 |
4 |
4 |
| Organic
acid, % min |
0.4 |
0.4 |
0.4 |
0.4 |
0.4 |
| acrylonitrile,
% |
14-17 |
17-20 |
17-20 |
24-27 |
24-27 |
| Produced:
Voronezh, Russia |
|
|
|
|
| |
Grade
26 |
Grade
26M |
Grade
33 |
Grade
33M |
Grade
40 |
Grade
40M |
Mooney
viscosity
ML 1+4 @ 100°C |
80-120 |
|
80-120 |
|
80-120 |
|
| ·
group 1 |
|
43-55 |
|
43-55 |
|
43-55 |
| ·
group 2 |
|
58-68 |
|
58-68 |
|
58-68 |
Tensile
strength,
MPa, min |
24 |
23.5 |
24 |
23.5 |
25.5 |
24.5 |
Elongation
at break,
%, min |
425 |
450 |
425 |
450 |
425 |
450 |
| Toluene
%, max |
34 |
34 |
30 |
30 |
20 |
20 |
| ash
content, %, max |
0.6 |
0.6 |
0.6 |
0.6 |
0.6 |
0.6 |
| Mass
loss on drying, % |
1 |
1 |
0.7 |
0.7 |
0.7 |
0.7 |
Antioxadant
total
mass, %: |
0.2-0.3 |
0.2-0.3 |
0.2-0.3 |
0.2-0.3 |
0.2-0.3 |
0.2-0.3 |
| Organic
acid, % max |
4 |
4 |
4 |
4 |
4 |
4 |
| Organic
acid, % min |
0.4 |
0.4 |
0.4 |
0.4 |
0.4 |
0.4 |
| acrylonitrile,
% |
27-30 |
27-30 |
31-35 |
31-35 |
36-40 |
36-40 |
| Produced:
Voronezh, Russia |
|
|
|
|
|
|